電阻焊設備在生產(chǎn)中，低碳鋼、中碳鋼、高碳鋼、低合金鋼及其組合一類(lèi)鋼焊接，其標準化的選用可以參照上訴低碳鋼的焊接規范，點(diǎn)焊機焊接強度高合金鋼時(shí)，要增大摩擦力壓力和頂部壓力，并適當延長(cháng)摩擦時(shí)長(cháng)。

In the production of resistance welding equipment, for the welding of low-carbon steel, medium carbon steel, high carbon steel, low alloy steel and their combinations, the standardized selection can refer to the welding specifications of low-carbon steel. When welding high-strength high alloy steel with a spot welding machine, the friction pressure and top pressure should be increased, and the friction time should be appropriately extended.

點(diǎn)焊機焊接高溫強度區別比較大的異種鋼或某些不會(huì )產(chǎn)生脆性合金層的異種金屬時(shí)，除開(kāi)在高溫下強度低的材料一方加一個(gè)模子以外，還要適當延長(cháng)摩擦時(shí)長(cháng)，提升摩擦壓力和頂鍛壓力。焊接擦汗女生脆性合金層的異種金屬時(shí)，需要采用模子封閉街頭金屬，降低焊接速度，增大摩擦力壓力和頂鍛壓力。

When welding dissimilar steels with significant differences in high-temperature strength or certain dissimilar metals that do not produce brittle alloy layers, in addition to adding a mold to the material with low strength at high temperatures, the friction time should also be appropriately extended to increase the friction pressure and forging pressure. When welding dissimilar metals in the brittle alloy layer of female sweaters, it is necessary to use molds to seal the street metal, reduce welding speed, increase friction pressure, and upset pressure.

焊接大直徑工件時(shí)在摩擦速度不變的前提下，應相應的降低轉速，。工件直徑擴大，摩擦壓力在摩擦表面上那個(gè)分布不均，摩擦變形阻力擴大，變形層的擴展要較長(cháng)的時(shí)間。因而在確保摩擦變形量不變的前提下，要比較大的摩擦壓力或比較長(cháng)的摩擦時(shí)長(cháng)。點(diǎn)焊機焊接不一斷面的碳鋼和低合金鋼工件時(shí)，因為導熱標準不一樣，在接頭上溫度分布和變形層的厚度不一樣，為了確保焊接質(zhì)量，應當選用強規范焊接。

When welding large-diameter workpieces, the rotational speed should be correspondingly reduced while the friction speed remains constant,. The diameter of the workpiece increases, the distribution of friction pressure on the friction surface is uneven, the frictional deformation resistance increases, and the expansion of the deformation layer takes a longer time. Therefore, while ensuring that the frictional deformation remains constant, it is necessary to have a relatively large frictional pressure or a relatively long frictional duration. When welding carbon steel and low alloy steel workpieces with different cross-sections using a spot welding machine, due to different thermal conductivity standards, the temperature distribution and thickness of the deformation layer on the joint are different. In order to ensure welding quality, strong standard welding should be selected.

焊接中碳鋼。高碳鋼和低合金鋼時(shí)，為避免焊縫中獲得卒火組織，降低焊后回火處理工序，應選擇較弱的焊接規范。點(diǎn)焊機焊接管道時(shí)，為減少內毛刺，在確保焊接質(zhì)量的前提下，應想方設法減小摩擦變形量和頂鍛變形量。

Welding medium carbon steel. When using high carbon steel and low alloy steel, in order to avoid obtaining a quenching structure in the weld and reduce the post weld tempering process, weaker welding specifications should be selected. When welding pipelines with spot welding machines, in order to reduce internal burrs and ensure welding quality, efforts should be made to reduce friction deformation and top forging deformation.

本文由山東自動(dòng)焊接設備友情奉獻.更多有關(guān)的知識請點(diǎn)擊:http://www.aplwebs.com真誠的態(tài)度.為您提供為的服務(wù).更多有關(guān)的知識我們將會(huì )陸續向大家奉獻.敬請期待.

This article is a friendly contribution from Shandong Automatic Welding Equipment. For more related knowledge, please click: http://www.aplwebs.com Sincere attitude. We will provide you with comprehensive service. We will gradually contribute more relevant knowledge to everyone. Stay tuned